[1]崔双双,郭晓慧,罗天凤,等.湿热环境下低吸水率玻化微珠保温砂浆配合比研究[J].福建理工大学学报,2024,22(03):213-218.[doi:10.3969/j.issn.2097-3853.2024.03.002]
　CUI Shuangshuang,GUO Xiaohui,LUO Tianfeng,et al.Study on mix ratio of low water absorption vitrified beads insulating mortar in hydrothermal environment[J].Journal of Fujian University of Technology;,2024,22(03):213-218.[doi:10.3969/j.issn.2097-3853.2024.03.002]
点击复制

湿热环境下低吸水率玻化微珠保温砂浆配合比研究()
分享到：

《福建理工大学学报》[ISSN:2097-3853/CN:35-1351/Z]

卷:
第22卷
期数:
2024年03期
页码:
213-218
栏目:
出版日期:
2024-06-25

文章信息/Info

Title:
Study on mix ratio of low water absorption vitrified beads insulating mortar in hydrothermal environment
作者:
崔双双; 郭晓慧; 罗天凤; 王旭
福建理工大学土木工程学院
Author(s):
CUI Shuangshuang;  GUO Xiaohui;  LUO Tianfeng;  WANG Xu
School of Civil Engineering, Fujian University of Technology
关键词:
湿热环境; 低吸水率; 玻化微珠水泥基材料; 配合比试验
Keywords:
hydrothermal environment;  low water absorption;  vitrified beads cement-based materials;  mix ratio test
分类号:
TU528.041
DOI:
10.3969/j.issn.2097-3853.2024.03.002
文献标志码:
A
摘要:
为解决东南沿海地区显著的风驱雨(WDR) 现象易引起的建筑外墙渗水、墙体材料劣化等问题,通过两阶段共14 组配合比试验,配制了一种低吸水率的外墙玻化微珠水泥基材料,研究了其在湿热环境下累计吸水量与吸水后导热系数的变化规律。研究结果表明:与混凝土相比,玻化微珠水泥基材料可以显著降低材料的导热系数、吸水量,热工性能优异,玻化微珠保温砌块可以有效提高砌块的热工性能,但也会降低材料抗压强度。与混凝土相比,玻化微珠水泥基材料的导热系数、7 d 累计吸水量和吸水7 d 后导热系数分别为0.336 W/ (m·K)、185.8 g 和0.483 W/ ( m·K),分别是混凝土的26.4%、62.4%和30.1%,吸水7 d 后导热系数增大0.147W/ (m·K),增幅为混凝土的44.3%。
Abstract:
In order to address the significant issue of wind driven rain (WDR) phenomenon in the southeastern coastal areas, which can easily cause water seepage on building exterior walls and deterioration of wall materials, a total of 14 groups of mix proportion tests were carried out in two stages. A low-water-absorption vitrified beads cement-based material for exterior walls was prepared and studies were conducted about the changes in thermal properties such as water absorption rate and thermal conductivity after water absorption in humid and hot environments. Research results indicate that compared with concrete, vitrified beads cement-based materials can significantly reduce the thermal conductivity and water absorption of the material, showing excellent thermal performance. Vitrified beads insulation blocks can effectively improve the thermal performance of blocks, but also reduce the compressive strength of the materials. Compared with ordinary concrete, the thermal conductivity, cumulative water absorption after 7 days, and thermal conductivity after 7 days of water absorption of vitrified microsphere cement-based materials are 0.336 W/(m·K), 185.8 g, and 0.483 W/(m·K), respectively, which are 26.4%, 62.4%, and 30.1% of those of concrete respectively. After 7 days of water absorption, the thermal conductivity increases by 0.147W/(m·K), which is 44.3% of that of concrete.

参考文献/References:

［1］ 杨金龙，米海惠，苏振国，等. 含水率对建筑外墙保温材料导热性能的影响［J］. 建筑材料学报，2017，20（6）：986-990. ［2］ OROSZ M，NAGY B，TTH E. Hygrothermal behavior of ultra-lightweight polystyrene concrete［J］. Pollack Periodica，2017，12（2）：53-66. ［3］ 江威，刘倩，曲军辉. 保温材料自然气候模拟条件下导热系数的研究［J］. 绿色环保建材，2020（9）：1-2. ［4］ 袁伟力. 稻草-混凝土复合自保温砌块综合性能研究［D］. 重庆：西南大学，2021. ［5］ 王亮. 气凝胶膨胀珍珠岩保温材料的研究及其建筑能耗分析［D］. 太原：太原理工大学，2019. ［6］ DAVRAZ M，KORU M，AKDAG A E. Numerical and experimental investigation of the effect of foam concrete as filler on design thermal conductivity of lightweight masonry block［J］. Journal of Thermal Analysis and Calorimetry，2019，137（6）：1867-1875. ［7］ 方正. 保温砂浆的湿热性能研究［D］. 长沙：湖南大学，2008. ［8］中华人民共和国住房和城乡建设部. 建筑砂浆基本性能试验方法标准：JGJ/T 70—2009［S］. 北京：中国建筑工业出版社，2009. ［9］ 国家质量监督检验检疫总局，中国国家标准化管理委员会. 绝热材料稳态热阻及有关特性的测定 防护热板法：GB/T 10294—2008［S］. 北京：中国标准出版社，2009.［10］ 郭宇菲. 自保温隔热混凝土力学性能与导热系数试验研究［J］. 安徽建筑，2019，26（1）：172-173，184.