[1]叶晓云,肖雪清,陈丁桂,等.超声辅助下聚丙烯酸/丙烯酰胺高吸水性树脂的合成研究[J].福建工程学院学报,2014,12(06):546-550.[doi:10.3969/j.issn.1672-4348.2014.06.008]
　Ye Xiaoyun,Xiao Xueqing,Chen Dinggui,et al.Study on synthesis of poly acrylic acid/ acrylamide superabsorbent resin under ultrasonic irradiation[J].Journal of FuJian University of Technology,2014,12(06):546-550.[doi:10.3969/j.issn.1672-4348.2014.06.008]
点击复制

超声辅助下聚丙烯酸/丙烯酰胺高吸水性树脂的合成研究()
分享到：

福建工程学院学报[ISSN:2097-3853/CN:35-1351/Z]

卷:
第12卷
期数:
2014年06期
页码:
546-550
栏目:
出版日期:
2015-01-25

文章信息/Info

Title:
Study on synthesis of poly acrylic acid/ acrylamide superabsorbent resin under ultrasonic irradiation
作者:
叶晓云; 肖雪清; 陈丁桂; 黄旭方
福建工程学院材料科学与工程学院
Author(s):
Ye Xiaoyun;  Xiao Xueqing;  Chen Dinggui;  Huang Xufang
College of Materials Science and Engineering, Fujian University of Technology
关键词:
超声波;  高吸水性树脂;  吸水率;  丙烯酸;  丙烯酰胺
Keywords:
ultrasonic irradiation;  superabsorbent resin;  absorbency;  acrylic acid;  acrylamide
分类号:
TQ630.4
DOI:
10.3969/j.issn.1672-4348.2014.06.008
文献标志码:
A
摘要:
借助超声波的分散、辅助引发作用，以 丙烯酸（ AA ）和丙烯酰胺（ AM ）为单体，以 N, N’- 亚甲基双丙烯酰胺 (NMBA) 为交联剂，以过硫酸钾 (K2S2O8) 为引发剂，无氮气保护下，采用超声波细胞粉碎法制备了聚 ( 丙烯酸 - 丙烯酰胺 )(P(AA-AM)) 高吸水性树脂。采用正交试验研究了树脂吸水性能最优的反应条件。通过单因素实验，重点考察了反应温度、引发剂用量、单体配比等对树脂吸水率的影响。用红外光谱（ FTIR ）和扫描电镜（ SEM ）对树脂的结构与形貌进行表征。结果表明，在超声条件下，可在较短的反应时间内合成高吸水性树脂。最佳工艺条件是 AA 中和度 =70% ， T=50 ℃ ， n(AM) : n(AA)=0.3 ， m(NMBA) : m( AA+AM ) =0.05% ， m(K2S2O8) : m( AA+AM )=0.2% ，吸水倍率最高为 398.172 g/g 。三维网状结构的存在是树脂高吸水性的关键。
Abstract:
A superabsorbent resin copolymer with acrylic acid (AA) and acrylamide (AM) as monomers was prepared by ultrasonic irradiation under no nitrogen protection using N, N’–methylene-bis-acrylmide (NMBA) as crosslinker and potassium persulfate (K2S2O8 ) as initiator. The optimal absorption condition of the resin was investigated through the orthogonal design. The influence of reaction conditions such as reaction temperature, dosage of the initiator and monomer mole ratio on water absorbency was investigated by single factor experiment. The molecular structure and morphology of the resin were measured with Fourier-transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The results show that the superabsorbent resin copolymer was synthesized in a short reaction time under ultrasonic irradiation . Moreover, the absorbing power was 398.172 g.g -1 in the optimum condition. Concretely, the degree of neutralization of AA, the reaction temperature, the monomer mole ratio of AM and AA, the mass ratio of NMBA and monomers, as well as the mass ratio of K 2 S 2 O 8 were 70%, 50 ℃ , 0.3, 0.05% and 0.2%, respectively. The high water absorbability of the resin is closely related to its three-dimension network structure.

参考文献/References:

[1] 邹新禧. 超强吸水剂[M].北京:化学工业出版社,2002.
[2] Zhou W L, Zhang Y, Jin K M, et al. Synthesis and characterization of functionalized acrylicacrylamidebased superabsorbent gels[J]. J Appl Polym Sci,2009,114:2828-2836.
[3] 袁月,申锋,胡树文.后交联型聚丙烯酸/丙烯酰胺高吸水性树脂的研究[J].化工新型材料,2012,40(6):97-99.
[4] 陈育宏,曹爱年.聚丙烯酸盐高吸水树脂的合成[J].科技进展,2001,15(12):26-28.
[5] 罗志河,杨万泰,杨正根.紫外光引发制备高吸水树脂研究进展[J].高分子通报,2010(5):12-16.
[6] 谭德新,王艳丽,徐国财,等.不加引发剂微波法合成高吸水性树脂的性能研究[J].化工新型材料,2009,37(1):30-31.
[7] 来水利,韩武军,李斌强.微波辐射下聚丙烯酸-丙烯酰胺高吸水性树脂的制备[J].精细石油化工,2010,27(3):9-11.
[8] 葛华才,黄国荣,文庆炳.无引发剂下微波辐射法制备壳聚糖-丙烯酸高吸水材料[J].材料导报,2007,12(2):85-87.
[9] 王斌,马祥梅,尚启超.超声辐射下水溶性双丙酮丙烯酸胺-丙烯酰胺-丙烯酸共聚物的合成研究[J].山东化工,2011,40(4):34-36.
[10] 谭德新,王艳丽,徐国财,等.复合交联剂型高吸水树脂的超声制备与性能研究[J].涂料工业,2009,39(3):41-44.
[11] 乌兰.高吸水性树脂的吸水机理及制备方法[J].化学与黏合,2006,28(3):169-171.
[12] 吴季怀,林建明,魏月琳.高吸水保水材料[M].北京:化学工业出版社,2005.

更新日期/Last Update: 2014-12-25